| Item | aluminum billet |
| series | 2xxxx,5xxx,6xxx,7xxx |
| character | utilitzing aerospace manufacturing technology of multi stage purification,grading homogenization ,special fine crystallization and SPC control in the manufacturing process. |
| Applications | aerospace,marine,automotive,railway transportation,oil and chemical industries etc |
| processing technic | casted,extruded |
| Surface | Degreased, anodized, mill finis,laminating,etc |
| MOQ | 2 tons |
| Delivery time | 15-20 days after confirming order |
| payment | 15~ 30% TT as deposit , the balance after you checked the quality before shippment |
| Packing | Export standard packing : PP bag , wooden box or other packing according clients request |
| alloy | standard | Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Zr | Ti | reference | |
| 2A12 | chinese standard | 0.5 | 0.5 | 3.8-4.9 | 0.3-0.9 | 1.2-1.8 | / | / | 0.3 | / | 0.15 | ||
| 2A14 | chinese standard | 0.6-1.2 | 0.7 | 3.9-4.8 | 0.4-1.0 | 0.4-0.8 | / | / | 0.3 | / | 0.15 | ||
| 2A50 | chinese standard | 0.7-1.2 | 0.7 | 1.8-2.6 | 0.4-0.8 | 0.4-0.8 | / | / | 0.3 | / | 0.02-0.1 | ||
| 2A70 | chinese standard | 0.35 | 0.9-1.5 | 1.9-2.5 | 0.2 | 1.4-1.8 | / | 0.9-1.5 | 0.3 | 0.9-1.5 | 0.1-0.25 | 0.02-0.1 | |
| 2219 | chinese standard | 0.2 | 0.3 | 5.8-6.8 | 0.2-0.4 | 0.02 | / | / | 0.1 | 0.02-0.1 | GB/T | ||
| 5A06 | chinese standard | 0.4 | 0.4 | 0.1 | 0.5-0.8 | 5.8-6.8 | / | / | 0.2 | 0.05-0.15 | 3190-2008 | ||
| 5A12 | chinese standard | 0.3 | 0.3 | 0.05 | 0.4-0.8 | 8.3-9.6 | / | / | 0.2 | 0.15 | |||
| 5083 | chinese standard | 0.4 | 0.4 | 0.1 | 0.4-1.0 | 4.0-4.9 | 0.05-0.25 | / | 0.25 | 0.15 | |||
| 6061 | chinese standard | 0.4-0.8 | 0.7 | 0.14-0.4 | 0.15 | 0.8-1.2 | 0.04-0.35 | / | 0.25 | 0.15 | |||
| 6A02 | chinese standard | 0.5-1.2 | 0.5 | 0.2-1.6 | 0.15-0.35 | 0.45-0.9 | / | / | 0.2 | 0.15 | |||
| 6082 | chinese standard | 0.7-1.3 | 0.5 | 0.14-0.4 | 0.4-1.0 | 0.6-1.2 | 0.25 | / | 0.2 | 0.1 | |||
| 7050 | chinese standard | 0.12 | 0.15 | 2.0-2.6 | 0.1 | 1.9-2.6 | 0.04 | / | 5.7-6.7 | / | 0.08-0.15 | 0.06 | |
| 7A52 | chinese standard | 0.25 | 0.3 | 0.05-0.2 | 0.2-0.5 | 2.0-2.8 | 0.15-0.25 | / | 4.0-4.8 | 0.05-0.15 | 0.05-0.18 | ||
| 7A04 | chinese standard | 0.5 | 0.5 | 1.4-2.0 | 0.2-0.6 | 1.8-2.8 | 0.1-0.25 | / | 5.0-7.0 | 0.1 |
| Typical alloy | temper | diameter |
| 2A12 | Homogenzation | |
| 2A14 | ||
| 2A50 | 166;220 | |
| 2219 | 380;396 | |
| 5A06 | 448;462 | |
| 5A12 | 566;582 | |
| 5083 | 915;1060 | |
| 6061 | 1220;1320 | |
| 6A02 | ||
| 6082 | ||
| 7050 | ||
| 2A12 | O,T3,T4,T6,H112 | 40-350 |
| 2A14 | ||
| 2A50 | ||
| 2219 | ||
| 5A06 | ||
| 5A12 | ||
| 5083 | ||
| 6061 | ||
| 6060 | ||
| 6063 | ||
| 6A02 | ||
| 6082 | ||
| 7A52 | ||
|
7A04 |
| Alloy | temper | The depth of coarse-grain | Typical dia | Tensile strength Rm(mpa) | Yield strength Rp0.2(Mpa) | Elongation A(%) | NDT | Reference | ||
| Not less than |
GJB 3539-1999 GBT 3191-1998 |
|||||||||
| 2A12 | 1 | ≤8 | 20-350 | 410 | 275 | 8 | A | |||
| 2A14 | H112 | ≤8 | 20-350 | 430 | ---- | 10 | A | |||
| 2A70 | H112 | ≤8 | ≤150 | 355 | ---- | 8 | A | |||
| 2A50 | H112 | ≤8 | 20-350 | 350 | ---- | 8 | A | |||
| 2219 | T1 | ≤8 | 20-350 | 370 | 255 | 8 | B | |||
| 5A06 | H112 | ≤8 | 20-350 | 315 | 155 | 15 | A | |||
| 5A12 | H112 | ≤8 | 20-350 | 370 | 185 | 15 | A | |||
| 6061 | H112 | ≤8 | 20-350 | 260 | 240 | 9 | A | |||
| 6A02 | H112 | ≤8 | 20-350 | 280 | ---- | 8 | A | |||
| 7A04 | 01 | ≤8 | 20-350 | 510 | 400 | 5 | A | |||